Quikrete Concrete Patcher Wall Edge How To

Water cure the concrete for a minimum of 3 5 days using a fine water mist.

Quikrete concrete patcher wall edge how to.

With proper attention to surface prep. Roughly smooth up with a trowel then cut around any forms with an edger. Dries quickly to a durable and flexible finish. Quik tip this step can be eliminated by applying quikrete acrylic concrete cure n seal to freshly placed concrete with a brush roller or garden sprayer.

Mix vinyl concrete patcher by adding about 10 ounces of water per 5 pounds of vinyl concrete patcher the vinyl concrete patcher should be poured into the mixing water. This video shows you how to make thin repairs to or patch damaged concrete using quikrete concrete patching compound. Made of a special blend of exterior grade vinyl resin fine sand and portland cement. Quikrete vinyl concrete patcher no.

Pre mixed concrete patch prep pressure wash area step 1 grab a trowel and lay it down step 2 smooth to edges with a trowel step 3 feather applica. Once the surface turns dull smooth and compact the concrete with a trowel. Vinyl concrete patcher is made of a special blend of vinyl resin fine sand and portland cement. 1133 is a multi purpose concrete repair material with strong adhesive properties.

Vinyl concrete patcher is ideal for making smooth repairs to crack or chipped concrete floors sidewalks or steps. Mix the quick setting cement using a margin trowel by adding 5 parts cement to 1 part quikrete acrylic fortifier until a lump free putty consistency is achieved. In addition to helping the curing process the sealer also protects the concrete border from stains. Quikrete concrete patching compound no.

It has strong adhesive properties allowing it to be applied down to a featheredge. It is important not to add more water or acrylic fortifier after the material has begun to set. Trowels to a feather edge of 1 16 1 6 mm. Allow the concrete to stiffen slightly waiting until all water has evaporated from the surface.

The more water that is added during the mixing process the weaker the bond strength and compressive strength will be.